2. The sketch shows a round bar with a groove loaded in bending. The material is annealed AISI 1040 steel, with an as-machined groove, and is to be designed with a reliability of 99%. (Note: This is a large shaft.) (a) What is the endurance limit of this specimen? Sz= k, cs kr kn Se (b) Estimate the safety factor using the Goodman line if the moment varies from-2000 Nm to +3630 Nm. AISI 2 S - 3Sompn

2. The sketch shows a round bar with a groove loaded in bending. The material is annealed AISI 1040 steel, with an as-machined groove, and is to be designed with a reliability of 99%. (Note: This is a large shaft.) (a) What is the endurance limit of this specimen? Sz= k, cs kr kn Se (b) Estimate the safety factor using the Goodman line if the moment varies from-2000 Nm to +3630 Nm. AISI 2 S - 3Sompn

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

2 Estimate the fatigue strength of a rotating-beam made of AISI 1035 CR steel corresponding to a life of 10° cycles of stress reversal. Also, estimate the life of the specimen corresponding to stress amplitude of 60 ksi.
Given: A ground steel rod with known diameter d is operating at temperature T. You are designing under bending loads. Use the following parameters in your analysis: d = 12 mm, T = 500°C,99% reliable, Sut 300 MPa. Find: a. Determine the endurance strength of the material. b. Determine the strength of the material at 104 cycles.
a rectangular stepped bar is shown. the bar is loaded in bending. determine the fatigue stress concentration factor if the ultimate stress of the material is 690 mPa. please inlcude how to calculate the notch sensitivity.
Estimate the fatigue strength of a rotating-beam made of AISI 1020 HR steel corresponding to a life of 12.5 kilocycles of stress reversal. Also, estimate the life of the specimen corresponding to stress amplitude of 36 ksi.
A solid round bar with diameter of 2 in has a groove cut to a diameter of 1.8 in, with a radius of 0.1 in. The bar is not rotating. The bar is loaded with a repeated bending load that causes the bending moment at the groove to fluctuate between 0 and 25 000 lbf in. The bar is hot-rolled AISI 1095, but the groove has been machined. Determine the factor of safety for fatigue based on infinite life and the factor of safety for yielding. Plars & .
1. Estimate the endurance strength of a 1.5-in-diameter rod of AISI 1040 steel having a machine finish and heat-treated to a tensile strength of 110kpsi, loaded in rotating bending.
A solid round bar with diameter of 2 in has a groove cut to a diameter of 1.8 in, with a radius of 0.1 in. The bar is not rotating. The bar is loaded with a repeated bending load that causes the bending moment at the groove to fluctuate between 0 and 25 000 lbf in. The bar is hot-rolled AISI 1095, but the groove has been machined. Determine the factor of safety for fatigue based on infinite life and the factor of safety for yielding. .
a) A bar of normalized AISI 4130 is subjected to a steady torsional stress of 103 MPa, an alternating torsional stress of 69 MPa, and alternating bending stress of 83 MPa. It has an endurance limit of 276 MPa. Using Gerber and ASME-elliptic criteria, find the safety factors guarding against a fatigue failure and the expected life of the part. Analyse your results. b) A bar of 25 mm diameter cold-drawn SAE 1045 steel is loaded in rotating bending. Determine its endurance limit or strength.
Carbon Steel L=100mm dsmall= 20mm moment of inertia ratio between stepped cross-sectional area = 1:2 F=2500 N at A and a fillet radius at the step of 2mm -loading cycles that the design can withstand before fatigue failure - calculate cycles using goodman line and max stress from static analysis. -determine the effect of the 2mm fillet ratio on the fatigue analyisis. constant force at A
To the ends of the hacksaw in the figure, the saw P=400N forcing the ends to open Forcing P=100N variable forces are acting. Brinell Hardness of the frame part of the saw 180MPa and t=10mm, the saw was produced by cold drawing. The saw, which will operate at ambient temperature, will cause fatigue. will consider the counter analysis of the x-x cross-sectional region Goodman fatigue damage for 50% reliability. using the criteria. I=bh3/12
Q2/ A steel bolt 0.005 m² in cross-section is subjected to a Static mean load of load of 200KN. What Value of Completely reversed direct fatigue load will Produce failure in 10² Cycles? Use the GERBER relationsip and assume that the Yield sureg. Strength of the steel is 400 MN/M² and the Stress required to produce. failure at 107 Cycles under Zero mean stress Condition is 300 MN/m².
The following results were obtained in a tensile test on a mild steel specimen of original diameter 28 mm and gauge length 56 mm. Load at limit of proportionality : 96 kN Extension at 96 kN load : 0.068 mm Load at yield point : 105 kN Maximum load : 170 kN When the two parts were fitted together after being broken, the length between gauge length was found to be 65.8 mm and the diameter at the neck was 18.8 mm. Calculate: (a). E, (b).σy, (c).σu, (d). PRIA and PE