(a) The Fe-C phase diagram is show in Figure Q5(a). Answer the following questions based on the phase diagram. (i) The microstructure of an iron-carbon alloy consists of proeutectoid ferrite and pearlite; the mass fraction of these two phases are 0.28 and 0.72, respectively. Determine the concentration of carbon in this alloy. (ii) What is the carbon concentration in the eutectoid and proeutectoid ferrite of a Fe-0.2 wt%C alloy? (iii) Schematically sketch the microstructures of hypocutectoid and hypereutectoid steels at room temperature. T(°C) 1600 1400 y+L A I+Fe.C 1200 (austenite) 100아 1148°C y+Fe,C 800 727°C 60아 a+Fe,C 4004 0.022 0.75 6.7 C, wt% C Figure Q5(a) Fe-C phase diagram *4.30 6 Fe,C (cementite)

(a) The Fe-C phase diagram is show in Figure Q5(a). Answer the following questions based on the phase diagram. (i) The microstructure of an iron-carbon alloy consists of proeutectoid ferrite and pearlite; the mass fraction of these two phases are 0.28 and 0.72, respectively. Determine the concentration of carbon in this alloy. (ii) What is the carbon concentration in the eutectoid and proeutectoid ferrite of a Fe-0.2 wt%C alloy? (iii) Schematically sketch the microstructures of hypocutectoid and hypereutectoid steels at room temperature. T(°C) 1600 1400 y+L A I+Fe.C 1200 (austenite) 100아 1148°C y+Fe,C 800 727°C 60아 a+Fe,C 4004 0.022 0.75 6.7 C, wt% C Figure Q5(a) Fe-C phase diagram *4.30 6 Fe,C (cementite)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In Figure 1 (phase diagram), an alloy composition of 95 wt% Mg and 5 wt% Al is cooled from 700 C to 475 C. An analysis of the resulting ε solid-phase composition reveals that it has a higher Mg content than is anticipated by the phase diagram.a) Explain why this might be the case and how your reasoning results in the higher-than-expected Mg content.b) Provide a sketch showing the likely distribution of Mg content within the volume of ε solid-phase.
A lead-tin (Pb-Sn) alloy of composition 30 wt % Sn and 70 wt % Pb is slowly heated from a temperature of 140 OC. Refer to the phase diagram provided in Figure 1 and answer the following. (i) At what temperature does the first liquid phase form? (ii) What is the composition of this liquid phase? (iii) At what temperature does complete melting of the alloy occur? (iv) What is the composition of the last solid remaining prior to complete melting?
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
According to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105
Draw thermal equilibrium diagram for the binary alloy system (Si-Au), from the following data:- a- Silicon melts at 1414 °C, and gold melts at 1064 °C. b-Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au, and identify all phases are present in the diagram c-Determine the amount of each phase for the alloy which consist of 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?
In the binary phase diagram for the Cu-Ni system in the Figure provided: 1. Draw the microstructures for each point for the alloy upon cooling (A-E) and label ALL phases! 2. What are the compositions (C's) of EVERY phase and the relative phase amounts (W's) for each microstructure A-E? Show all work! TOCL (liquid) 20 (a, solid) 30 A BCD E E 40 OOOOO 50 wt% Ni www CL= Ca= CL= Ca= CL= Ca= CL= Cu= C₁= Ca= W₁= Wa= WL= WQ= W₁= Wa= W₁= Wa= W₁= Wa= A B C D E
A 50 wt% Ni–50 wt% Cu alloy is heated to a temperature within the a liquid-phase region. If the composition of the alpha phase is 58 wt% Ni, determine (b) the composition of the liquid phase in wt% Ni
Construct the hy pothetical phase diagram for metal A and B between temperature of 600 C° and 1000 C° given the following information: The melting point of A is 940 Cº. The solubility of B in A is negligible at all temperatures The melting point of metal B is 830 Cº. The maximum solubility of A in B is 12%A, which occurs at 700 Co. At 600 C°, the solubility of A in B is 8%A. One eutectic occurs at 700 C° and 75%B. A second eutectic occurs at 730 C° and 60%B. A third eutectic occurs at 755 C° and 40%B. One congruent melting point occurs at 780 C° and 51%B. A second congruent melting point occurs at 755 C° and 67%B. There exist two intermetallic compounds: AB at 51%B and AB2 at 67%B. Note all composition are in weight percent.
Refer to Figure 1 showing the phase diagram for the Fe-Fe3C system. Consider 1.0 kg of austenite containing 1.15 wt% C, cooled to below 727 C (1341 F). What is the proeutectoid phase? How many kilograms each of total ferrite and cementite form? How many kilograms each of pearlite and the proeutectoid phase form? Schematically sketch and label the resulting microstructure.
The figure below shows Pb-Sn phase diagram. What is the composition of Pb and Sn at point 1? 1200 1000 Liquid a +L 779 C (Tg) B+L 6 800 8.0 71.9 G 91.2 600 400 200 20 40 60 80 100 (Pb) Composition (wt% Sni (Sn) Callister Jr., W.D., 2007 O a. 80 wt % Sn and 20 wt % Pb O b. 10 wt % Sn and 90 wt % Pb O c. 90 wt % Sn and 10 wt % Pb O d. 20 wt % Sn and 80 wt % Pb Temperature ("C)
For an alloy containing 20 wt % Ag, refer to the Cu-Ag phase diagram given in the Figure: What is the melting point of Cu in °C? What are the relative amounts(in %) of the existing phases at 900°C? Define the Eutectic point in terms of °C and the composition % of Ag.
BINARY PHASE DIAGRAMS Please only answer parts d and e as the rest have been solved. Show full detailed explanation to answers with diagrams if necessary a)(i) What is the melting point of pure Mg?(ii) What is the maximum solubility of Mg in Pb and at what temperaturedoes this occur? (b) A 50 wt.% Pb-50wt% Mg alloy is slowly cooled from 700 °C to 400 °C.(i) At what temperature does the first solid phase form?(ii) What is the composition of this solid phase?(iii) At what temperature does all the liquid solidify?(iv) What is the composition of the last remaining liquid phase?(v) What is the freezing range? (c) What is the mass fraction of solid and liquid of a 60 wt.% Mg alloy at atemperature of 500 °C.(d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C.(e) A Mg-Pb alloy of mass 5.5 kg has a composition just slightly below thesolubility limit of 200 °C.(i) What mass of lead is in the alloy?(ii) If the alloy is heated to 350 °C how much more lead can be dissolvedin…