An 80 wt% Cu - 20 wt% Ni alloy is slowly cooled from 1250 °C to 1100 °C. T(°C) 1600 L (liquid) 1500 Cu-Ni 1400 solidus a phase diagram liquidus 1300 (FCC solid solution) 1200 1100 1000 20 40 60 100 wt% Ni 80 What is the composition of the last remaining liquid phase?

An 80 wt% Cu - 20 wt% Ni alloy is slowly cooled from 1250 °C to 1100 °C. T(°C) 1600 L (liquid) 1500 Cu-Ni 1400 solidus a phase diagram liquidus 1300 (FCC solid solution) 1200 1100 1000 20 40 60 100 wt% Ni 80 What is the composition of the last remaining liquid phase?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, i. State the name of phase(s) present. ii. Calculate the composition(s) of the phase(s) present. 600 300 Liquid 500 a+L 200 400 300 100 200 100 20 60 100 (Pb) (Sn) Composition (wt % Sn) Temperature ("C) Temperature ("F)
A 50 wt% Ni–50 wt% Cu alloy is heated to a temperature within the a liquid-phase region. If the composition of the alpha phase is 58 wt% Ni, determine (b) the composition of the liquid phase in wt% Ni
A binary alloy having 28 wt% Cu and balance Ag solidifies at 779°C. The solid consists of two phases a and B. Phase a has 9% Cu whereas phase ß has 8 % Ag at 779°C. At room temperature these are pure Ag and Cu respectively Sketch the phase diagram. Label all phases and temperatures. The melting points of copper and silver are 1083 and 9610 respectively s Pà) Estimate the amount of a and B in the above alloy at 779°C and at room temperature.) b) Calculate the mass fraction of phases for 40% Cu alloy at 300 °C and TR c) What is the composition of the alloys in (b)
2: Consider a Cu-80wt% Ni-20% alloy, determine the following: (a) The liquidus and solidus temperature of alloy. (b) The composition of last liquid to solidify. (c) The composition of last solid to melt. (d) The composition of the solid and liquid phases at 1175 °C. (Draw the microstructure at this points) (e) The amount of the solid and liquid phases at 1175 °C. Composition (at% Ni) 20 40 60 80 100 1600 2800 1500 Liquid 1453 C 2600 1400E Solidus line Liquidus line 2400 1300 1200 2200 1100 2000 1085 C 1000 20 40 60 80 100 (Cu) Composition (wt% Ni) (Ni) Temperature ("F)
Using the following table, draw a melting point diagram and estimate the eutectic temperature and composition: Percent composition Melting point range (°C) 100% A 125-126 75% A-25% B 115-120 65% A- 35% B 128-131 50% A- 50% B 135-140 100% B 151-152 Can you suggest what additional points you need to give a more accurate measure of the eutectic point?
rams A copper-nickel alloy of composition 75 wt% Ni-25 wt% Cu is slowly heated from a temperature of 1300°C (1573). (a) At what temperature does the first liquid phase form? (b) What is the composition of this liquid phase? T(°C) 1600 (c) At what temperature does complete melting of the alloy occur? (d) What is the composition of the last solid remaining prior to complete melting? 1500 1400 1300 1200 1100 1000 17 / 17 0 L (liquid) 20 liquidus + a solidus 100% 40 α (FCC solid solution) 60 80 100 wt% Ni 17
Calculate the weight fraction for phases at point B? what are those phases? Is there any eutectic rection? How many phases are present in this diagram? Cu-Ni system T(°C) TA 1300 -L (liquid): A tie ļine liquidus L +a Тв EB solidus (solid) 1200 TD ID 20 3032 35: 4043 50 Ca wt% Ni
(c) in the Cu and Ag phase diagram shown in Figure 1.1, consider an alloy composition of 40 wt% Cu - 60 wt% Ag. Composton Ca RD 20 1200 우 100 2200 2000 1000 pnbn- :000 1600 8.0 1400 912 :200 G00 Sous :000 400 G00 200 0 400 100 40 60 Composition rwts AD Figure 1.1: Cu - Ag Phase Diagram i. What Phases are present in the Alloy at 800° C? i. What are the compositions of present phases if the alloy is cooled by 20° C? iii. What are the mass fraction of phases? If the alloy was further cooled by 2° C, determine the volume fraction of the phases? Take the densities of Cu and Ag as 8.96 and 10.49 g/cm' respectively. iv.
In the binary phase diagram for the Cu-Ni system in the Figure provided: 1. Draw the microstructures for each point for the alloy upon cooling (A-E) and label ALL phases! 2. What are the compositions (C's) of EVERY phase and the relative phase amounts (W's) for each microstructure A-E? Show all work! TOCL (liquid) 20 (a, solid) 30 A BCD E E 40 OOOOO 50 wt% Ni www CL= Ca= CL= Ca= CL= Ca= CL= Cu= C₁= Ca= W₁= Wa= WL= WQ= W₁= Wa= W₁= Wa= W₁= Wa= A B C D E
A 50 wt% Pb-50 wt% Mg alloy is slowly cooled from 700 °C (1290 °F) to 400 °C (750 °F). (a) At what temperature does the first solid phase form? (b) What is the composition of this solid phase? (c) At what temperature does the liquid solidify? (d) What is the composition of this last remaining liquid phase? Temperature (°C) 700 600 500 400 300 200 100 2 0 0 (Mg) 560°C First solid (21 wt% Pb) α 20 465°C 5 a + L Composition (at% Pb) 40 10 L a + Mg₂Pb 20 60 Composition (wt% Pb) Last liquid (67 wt% Pb) 30 Mg₂Pb 40 T T L + Mg₂Pb M 18 80 L + Mg₂Pb 70 100 B B+ Mg₂Pb T B + L D T 1200 1000 800 600 400 200 100 (Pb) Temperature (°F)
Temperature ("C) Temperature ($1 Consider 1 kg of Copper - Silver alloy (Cu - Ag) containing 75 wt% Ag. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 778 °C (just below the eutectic temperature). Calculate the mass in kg of the eutectic phase B (phase B that appears during the eutectic reaction) that forms? Composition (at% Ag 20 40 60 100 2200 80 1200 2000 Liquidus 1000 LIquid 1800 Solidus 1600 800 779°C (T 80 91.2 1400 IC. 1200 600 Solvus T000 400 800 200 20 40 80 100 (Cu) Composioon wt A
In the binary phase diagram for the Cu-Ni system in the Figure provided: 1. Draw the microstructures for each point for the alloy upon cooling (A-E) and label ALL phases! 2. What are the compositions (C's) of EVERY phase and the relative phase amounts (W's) for each microstructure A-E? Show all work! T(°C) (liquid) L 20 (a, solid) 30 A BUD E 40 Co OOOOO w 10 50 wt% Ni CL= Ca= CL= Ca= CL= Ca= C₁= Cu= C₁= Ca= WL= Wa= WL= Wα= W₁= W= W₁= Wa= W₁= Wu= A B E