Figure P1.16 shows the stress–strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calculations and units): Proportional limit Yield stress at an offset strain of 0.002 in./in. Ultimate strength

Figure P1.16 shows the stress–strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calculations and units): Proportional limit Yield stress at an offset strain of 0.002 in./in. Ultimate strength

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter9: Time, Temperature, And Mechanical Properties

Section: Chapter Questions

Problem 9.3P

See similar textbooks

Related questions

Q: Q1) A specimen with the given dimension is loaded as given in the figure below. Determine; a) The…

A: As per the guidelines of Bartleby we are supposed to only answer the first three subparts of the…

Q: Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having…

A: Tensile yield strength :-yield strength of the material is the stress at a point at which material…

Q: A cylindrical rod AB has a length ? = 80 cm and a diameter of ? = 2 cm. The modulus of elasticity is…

A: Given Length of Rod, L=80cm Diameter of rod=2 cm Modulus of elasticity, E=200 GPa Force, P=100 kN…

Q: Table 1 shows the stress-strain data for a new polymeric material rod subjected to an axial load.…

A: Table shows the stress strain data for a new polymeric material rod subjected to an axial load .Now…

Q: 1.21 An elastoplastic material with strain hardening has the stress-strain relation shown in Figure…

Q: • Two Identical circular rods of same diameter and same length are subjected to same magnitude of…

Q: The stresses shown in the figure act at a point on the free surface of a machine component. If o =…

A: Given Stress in X direction for inclined plane = 31 Mpa

Q: Determine o - Determine the equivalent state of stress on an element if it is oriented 30° Express…

A: Stress is the average force per unit area and is a vector quantity. The stress at any point in a…

Q: Given that a steel cyInder of dimenslons 12.0 mm in dlameter and 70 mm bng is subjected to tensicn.…

A: a) According to Hook's law within the elastic limit, stress is directly proportional to strain.…

Q: Q5) A specimen of alloy having a rectangular cross section of dimensions 5 mm x 16 mm is deformed in…

A: Given:- dimensions-5mm x 16mm To find:- a)Modulus of elasticity b)Yield strength c)The modulus of…

Q: 1. The following data were obtained during a tension test of an aluminum alloy. The initial diameter…

A: The given data is: The initial diameter =0.505 in The gauge length=2.0 in

Q: The stress–strain diagram for a steel alloy having an original diameter of 0.5 in. and a gage length…

Q: Take oz = 84 MPa and Tzy = 35 MPa (Figure 1) Part A Determine the equivalent state of stress on an…

A: The given figure is shown below:

Q: SITUATION. As shown in the figure below, a rigid bar with negligible mass is pinned at O and…

Q: 650 600 550 500 450 400 350 300 250 200 150 100 50 0.002 0.004 0.006 0.008 0.01 0.012 0.014 0.016…

A: Stress loading and stress and strain relationship is given in the question and it has been asked to…

Q: The stress-strain curve of an alloy is given below. Calculate the modulus of toughness. 14 12 10…

Q: SITUATION. As shown in the figure below, a rigid bar with negligible mass is pinned at O and…

Q: Consider a cylindrical specimen of a steel alloy 10.0 mm in diameter and 75 mm long that is pulled…

A: the test is conducted in UTM. the test is standardized by American testing society material . the…

Q: An initially rectangular element of a material is deformed into the shape shown in the figure.…

Q: A tension test performed on a metal specimen to fracture produced the stress- strain relationship…

A: From the above graph, linear portion is up to the point where stress is equivalent to 50 ksi, and…

Q: 1.14 The stress-strain relation shown in Figure P1.14 was obtained during the ten- sile test of an…

A: The given stress-strain relationship of aluminum alloy

Q: Mechanics of Deformable Bodies Calculate the increase in stress for each segment of the compound bar…

Q: A typical aluminum-alloy scuba diving tank is shown. The outside diameter of the tank is 20 cm and…

Q: into the parallelogram shape as shown in the figure. All edges remain the same length a, as the…

A: solution of above problem is below:

Q: A part’s maximum Von Mises stress and materials are given below. Determine for each of these…

A: To determine whether given part is safe or not.

Q: Q.3 The following data were obtained from the tensile test of Aluminum alloy. The initial diameter…

A: Given data; Gauge length = 2 in Initial diameter = 0.505 in

Q: A thin sheet of rubber in the form of a square is uniformly deformed into the parallelogram shape as…

Q: The stresses shown in the figure act at a point on the free surface of a machine component. If o= 45…

Q: A tension test performed on a metal specimen to fracture produced the stress– strain relationship…

A: The given figure is shown below:

Q: A steel alloy specimen having a rectangular cross section of dimensions 19.1 mm x 3.1 mm (0.7520 in.…

Q: • Two Identical circular rods of same diameter and same length are subjected to same magnitude of…

Q: Figure P1.18 shows (i) elastic-perfectly plastic and (ii) elastoplastic with strain hardening…

A: Given: The stains are 0.001 and 0.004. Consider the below figure,

Q: A cylindrical steel alloy rod with a 0.5 in. diameter is subjected to tension.Determine the…

A: It is required to calculate the strain in the x-direction. Here, is the change in diameter, and do…

Q: A 19-mm reinforcing steel bar and a gauge length of 75 mm was subjected to tension, with the results…

A: Given: Diameter of steel bar d, is 19 mm. Gauge length l, is 75 mm. The table is given below,

Q: The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of…

A: Given that, Initial diameter of the specimen (D) =0.505inch Length of the specimn(L)= 2.0 inch…

Q: 3) The stress-strain curve of an alloy is given below. Calculate the modulus of toughness. 14 12 10…

Q: A cube made of an alloy with dimensions of 50 mm * 50 mm * 50 mm is placed into a pressure chamber…

A: Given data: Since pressure applied uniformly on all sides of the cube:

Q: In a material under a state of plane strain, a 10 x 10 mm square centred at a point gets deformed as…

Q: A round steel alloy bar with a diameter of 0.75 in. and a gauge length of 3.0 in. was subjected to…

A: Calculating area of steel bar: Substitute the value of D:

Q: Elastic Properties of Materials 6.15 A cylindrical specimen of steel having a di- O ameter of 15.2…

Q: 2.43.The distribution of stress in an aluminum machine component is given (in megapascals) by = y+…

Q: A tension test performed on a metal specimen to fracture produced the stress-strain relationship…

Q: A steel bar 100 mm long is subjected to a tensile stress o. If change in length of bar is 0.05 mm…

A: Given data- Length L=100 mm,change in length ∆L=0.05 mm,E=200 GPa, To Find- The value of stress…

Q: Following figure shows the stress-strain diagrams for three materials A, B and C. (Where, P = 200+X,…

Q: B C D 3. FIGURE QI(a)

A: It is required to classify the materials in order of largest to smallest strain hardening.

Q: A round steel alloy bar with a diameter of 19mm and a gauge length of 76mm was subjected to tension,…

A: Given data: Diameter of round steel alloy bar = D = 19 mm Gauge length = L = 76 mm Area of steel bar…

Q: A sample of tin alloy has the following stress-strain curve 400 200 Strain 0.05 0.10 0.15 0.20 From…

Q: A beam shown below, 200mm wide by 350mm deep, is loaded as shown in figure below. Determine the…

Q: Based on the figure below, a steel rod was fitted on the copper tube and was fixed with a washers…

Q: Q1/ Consider the brass alloy for which the stress-strain behavior is shown in the figure below. A…

A: (a) Calculate the elongation as; Stress=EBrass×StrainForceArea=EBrass×∆LL2250…

Concept explainers

Material Properties

Construction in civil engineering demands high strength, durability, and longevity. These targets can be achieved by better design and analysis, along with the correct choice of materials. Different materials have different properties and hence, they respond and performs differently under the various condition of external loadings. It is therefore a critical task of an engineer to select the right material based on the property that the material is supposed to function in real-time. When speaking about the property, there are different categories of material properties like chemical property, physical property, mechanical property, electrical property, magnetic property, thermal property, etc. These material properties form the basis of material selection in various applications.

Question

Figure P1.16 shows the stress–strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calculations and units):

Proportional limit
Yield stress at an offset strain of 0.002 in./in.
Ultimate strength
Modulus of resilience
Toughness
Which metal is more ductile? Why?

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step 3

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 3 steps with 3 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
1.17 Figure P1.17 shows the stress-strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calcu- lations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 in./in. 150 - - Metal A 100 • Metal B 50 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, in./in. FIGURE P1.17 c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? Stress, ksi
I5 In a tensile test experiment of carbon steel. a standard specimen (D= 0.505 in. Gauge length=2.0 in & total length 8 in) had a 0.2% offset yield strength of 80.000 psi and engineering strain of 0.010 at the yield strength point Calculate: The load (force) at this point. The instantaneous area of the specimen at this point. c. The true stress at this point. d. The true strain at this point. e. The total length of the specimen. if the load is released at this point.
S Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? 900 Metal A 600 Metal B 300 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, m/m FIGURE P1.16 Stress, MPa
Strain = 600 Stress = Strain = 500 Stress = 400 500 300 400 300 200 200 100 100 0.000 0.002 0.004 0.006 Strain 0.00 0.04 0.08 0.12 0.16 0.20 Strain Stress (MPa)
A steel 0.6 inch×1.2 inch steel 90 m long is subjected to a 45 KN tensile load along its lenght.If poison's ratio is 0.3 Find: A. The deformation along its lenght. B. The deformation along its thickness. C. The defirmation along uts width. D. The lateral strain.
PROBLEM 1 A steel rod with a cross sectional area of 150 mm? is stretched between two fixed points. The tensile load at 20°C is 5000 N. a.) What will be the stress at -20°C? b.) At what temperature will the stress be zero? Assume a = 11 .7 µm/m°C, and E = 200 Gpa *Show geometry of deformation ©sidewar
1.4-7 The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13 mm and a gage length of 50 mm (see figure for Prob. 1.4-3). At fracture, the elongation between the gage marks was 3.0 mm and the minimum diameter was 10.7 mm. Plot the conventional stress-strain curve for the steefor the steel and determine the proportional limit, modulus of elastics of elastic- ity (i.e., the slope of the initial part of the stress-strain,tress-strain curve), yield stress at 0.1% offset, ultimate stress, percent, elongation in 50 mm, and percent reduction in area. 'ess, percent area. TENSILE-TEST DATA FOR PROB. 1.4-7 Elongation (mm) 0.005 0.015 0.048 Load (kN) 5 10 30 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
The strain gauge measurement of a steel plate indicate the principle strains are 0.003 and 0.001. What is the value of major principle stress in MPa? (E = 200 GPa, μ = 0.33)
Problem 1 An aluminum rod is rigidly attached between a steel rod and a bronze rod as shown. Axial loads are applied at the positions indicated. Aluminum Steel A=800mm2 A=1000mm2 Bronze A=700mm? 4P 2P 500mm 600mm 700mm 1. What is the maximum value of P that will not exceed the axial stress bronze of 105 MPa? 2. What is the maximum value of P that will not exceed the axial stress in aluminum of 90 MPa? 3. If P=10KN, what is the axial force to be carried by the aluminum in KN? 4. If P is 5KN, what is the axial stress of steel?
In the figure shown below, determine: 1) The final temperature if the normal stress at aluminium is Og = -90 MPa and the initial temperature %3D 20°C. 2) The final length of the aluminium member. Aluminum A=1800mm? Bronze A=1500mm? E=73GPA E=105GPA a=23.2x10-6/°C a=21.6x10-6/°C Gap=0.5mm 0.35m 0.45m