For the metals A and B, which are given below, create the hypothetical phase diagram between 500 ° C and 900 ° C temperatures. The melting temperature of metal A is 840 ° C. The solubility of B in A can be ignored at all temperatures. Metal B has a melting temperature of 730 ° C. The maximum resolution of A in B is 10 wt% A, which occurs at 600 ° C. At 500 ° C, the solubility of A in B is 6% A by weight. A eutectic 600 ° C and 74% B by weight - 26% by weight A are formed. The second eutectic occurs at 630 ° C and 59% B - 41% A by weight. A third eutectic occurs at 655 ° C and 39% B - 61% A by weight. A congress melting point is formed at 680 ° C and 52% B - 48% A by weight. A second congress melting point is formed at 655 ° C and 66% B - 34% A by weight. The intermetallic compound AB is present at 52 wt% B - 48 wt% A. The intermetallic compound AB2 is present at 66 wt% B to 34 wt% A.
For the metals A and B, which are given below, create the hypothetical phase diagram between 500 ° C and 900 ° C temperatures.
The melting temperature of metal A is 840 ° C.
The solubility of B in A can be ignored at all temperatures.
Metal B has a melting temperature of 730 ° C.
The maximum resolution of A in B is 10 wt% A, which occurs at 600 ° C.
At 500 ° C, the solubility of A in B is 6% A by weight.
A eutectic 600 ° C and 74% B by weight - 26% by weight A are formed.
The second eutectic occurs at 630 ° C and 59% B - 41% A by weight.
A third eutectic occurs at 655 ° C and 39% B - 61% A by weight.
A congress melting point is formed at 680 ° C and 52% B - 48% A by weight.
A second congress melting point is formed at 655 ° C and 66% B - 34% A by weight.
The intermetallic compound AB is present at 52 wt% B - 48 wt% A.
The intermetallic compound AB2 is present at 66 wt% B to 34 wt% A.
![](/static/compass_v2/shared-icons/check-mark.png)
Trending now
This is a popular solution!
Step by step
Solved in 2 steps with 1 images
![Blurred answer](/static/compass_v2/solution-images/blurred-answer.jpg)
![Elements Of Electromagnetics](https://www.bartleby.com/isbn_cover_images/9780190698614/9780190698614_smallCoverImage.gif)
![Mechanics of Materials (10th Edition)](https://www.bartleby.com/isbn_cover_images/9780134319650/9780134319650_smallCoverImage.gif)
![Thermodynamics: An Engineering Approach](https://www.bartleby.com/isbn_cover_images/9781259822674/9781259822674_smallCoverImage.gif)
![Elements Of Electromagnetics](https://www.bartleby.com/isbn_cover_images/9780190698614/9780190698614_smallCoverImage.gif)
![Mechanics of Materials (10th Edition)](https://www.bartleby.com/isbn_cover_images/9780134319650/9780134319650_smallCoverImage.gif)
![Thermodynamics: An Engineering Approach](https://www.bartleby.com/isbn_cover_images/9781259822674/9781259822674_smallCoverImage.gif)
![Control Systems Engineering](https://www.bartleby.com/isbn_cover_images/9781118170519/9781118170519_smallCoverImage.gif)
![Mechanics of Materials (MindTap Course List)](https://www.bartleby.com/isbn_cover_images/9781337093347/9781337093347_smallCoverImage.gif)
![Engineering Mechanics: Statics](https://www.bartleby.com/isbn_cover_images/9781118807330/9781118807330_smallCoverImage.gif)