The yield point for a brass alloy that has an average grain diameter of 50 micrometers is 120 MPa. The yield point for a brass alloy that has an average grain diameter of 50 µm is 120 MPa. At a grain diameter of 10 µm, the yield point increases to 240 MPa. At whatgrain diameter (in µm) will the yield point be 200 MPa?

Answered: Image /qna-images/answer/e345d70c-14c4-4ba2-9be0-c11bfd9d2632.jpg

The yield point for a brass alloy that has an average grain diameter of 50 um is 120 MPa. At a grain diameter of 10 um, the yield point increases to 240 MPa. At what grain diameter (in um) will the yield point be 200 MPa?

The yield point for a brass alloy that has an average grain diameter of 50 um is 120 MPa. At a grain diameter of 10 um, the yield point increases to 240 MPa. At what grain diameter (in um) will the yield point be 200 MPa?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: The critical resolved shear stress for copper is 0.48 MPa. Determine the maximum possible yield…

Q: An 80μm diameter glass fiber is confirmed to have no surface cracks longer than 5μm. If the…

A: Given that, Diameter of glass, D=80 μm,Strength of fiber, σm=5 GPa=5000 MPa,Surface-crack length:…

Q: c) Sample of an aluminum alloy has a tensile strength of 175 MPa, What will be the maximum force…

Q: What physical reasons why reducing grain size is an effective alternative for increasing the…

A: Smaller grains have greater ratios of surface area to volume, which means a greater ratio of grain…

Q: A Cu-30% Zn brass plate, originally 1.20 inches thick, is desired to have a yield strength greater…

Q: Realizing that ductile materials fail by shear, what did Henri Trescapropose?

A: Henry Tresca theory: Tresca yield criteria is a theory for the failure for the ductile materials.…

Q: Sketch a diagram showing impact energy as a function of temperature, of (i) 0.1% carbon steel; (ii)…

A: given; sketch a diagram showing impact energy as a function of temperature of (i) 0.1% carbon steel…

Q: Your current carburizing process produces a case depth of 4 mm in 7 hours. If you want to increase…

Q: Assume that the critical stress intensity factor or fracture toughness ðKIcÞ for a partially…

Q: A single crystal of an FCC metal isoriented so that the [001] direction is parallel to an applied…

A: Data given- A single crystal of an FCC metal applied stress - 5000 psi a=[0 0 1] b= [1 1 1] c=[1` 1…

Q: 7.41 An uncold-worked brass specimen of average grain size 0.008 mm has a yield strength of 160 MPa…

Q: A sample is made of a făce-centered cubic (fcc) single crystal. The sample starts to have plastic…

A: Given: The stress along {012} direction = 100 MPa

Q: In the Figure below, the tensile breaking strength, (sigma mark)tenstile-breaking = 140 Mpa…

A: Given: The tensile strength of the material = 140 Mpa The compressive strength of the material = 460…

Q: In a sample made of an alloy that has not been subjected to cold forming, the average grain size is…

A: Yes, it is possible. Grain size is often determined by the rate at which the material cooled during…

Q: A single crystal of an FCC metal is oriented so that the [001] direction is parallel to an applied…

A: Data given- Single crystal of an FCC Metal applied stress=5000 psi a…

Q: With the aid of sketches compare and contrast the fatigue fracture appearance between an alloy that…

Q: Hilda, Layla, and Saber were experimenting with a carbon steel rod in the chemistry laboratory.…

Q: 3. An engineering ceramic has a flexure strength that obeys Weibull statistics with m = 15. If the…

A: Data given- m = 15 Pf1 = 0.3 Ps1 = 1-0.3 = 0.7 Ps2 = 0.4

Q: How much heavier, on average, will an aluminum-alloy tennis racquet be if it is made from titanium…

A: weight of the Aluminum bat=WAl weight of Titanium bat=WTi Assuming the rod to circular of diameter…

Q: Explain in detail what is the difference between creep and relaxation. Use Figure 8.

Q: When making hardness measurements, whether by nanoindentation or by conventional indentation…

A: A preexisting indent in the vicinity of the new indent influences the hardness value, thus resulting…

Q: Question 6 During an extrusion process, a chromium billet at a temperature of 1300°C, need to be…

A: Given DataUTSo=915MPaT=1300°Cd=13mmn=4P=16%

Q: Plot modulus of elasticity versus the volume percent of WC in Co from 0 to 100 vol%, using both…

A: To find :- Elastic curve graph

Q: Briefly explain, what are the modulus of elasticity and modulus of rigidity and the relationship…

A: Modulus of elasticity ; The Young modulus (elasticity modulus) is a quantity that describes the…

Q: What will be the maximum force that can be withstood

Q: 6) Would ceramic materials or metallic materials would have better creep resistance? Briefly explain…

A: As per bartleby guidelines we are allowed to solve only 1st question if multiple questions are…

Q: An 80μm diameter glass fiber is confirmed to have no surface cracks longer than 5μm. If the…

A: given; ⇒theoretical strength (τ1)=5GPa =5000Mpa⇒breaking…

Q: he critical resolved shear stress for copper is 0.48 MPa. Determine the maximum possible yield…

Q: Consider a single crystal oriented such that the slip direction and normal to the slip plane are at…

A: Given: Angles are: ϕ=42.7°λ=48.3° Critical resolved shear stress is, τR=27.1 Mpa

Q: The maximum principal strain failure criterion is appropriate for ceramic materials". Is this true…

A: As we know that Ceramic is a brittle material

Q: Explain the differences in the grain structure between a metal which has been cold worked and…

A: When the cold rolling process is done in any material than its shape is permanently changed due to…

Q: Glass ceramics have low coefficients of thermal expansion. State why this is the case (hint;…

A: given; Glass ceramics have low coefficients of thermal expansion. State why this is the case (hint;…

Q: 6. How do you increase the hardness of components being made from 0.8% carbon steel? Explain the…

A: We can increase the hardness of low carbon steel by the carburizing process.

Q: Under room temperature, why grain boundaries are beneficial for improving materials strength? How…

A: An interface between two surfaces is called the grain boundary. Due to grain boundaries the thermal…

Q: Draw a load vs. displacement curve as obtained from a homogeneous material using nanoindentation.…

A: Load vs Displacement curve-

Q: 141) How is the elastic modulus calculated? A) With the strain rate of strain B) The ratio of shear…

A: 141) A) Strain rate of strain defines the rate of change in strain in materials. B) The ratio of…

Q: Estimate the linear relationship between the Ultimate Tensile Strength and HBN for the range of…

A: here take linear line of brass alloys from strength Vs BHN diagram. Now locate extreme point of…

Q: In the experiment on the flexural strength of chocolates, what would happen when the load is…

A: Flexural strength is a measure of the failure stress in bending.

Q: 7. The tensile strength of polycrystalline spinel can be appi Petch relation. If the spinel has a…

A: Write the expression for hall patch relation.

Q: List and define the properties required for a material to be deformed

A: The property required for a material to be deformed are 1. Ductility 2.malleability

Q: Write the slip systems of the metals with crystal structures of BCC, FCC and HCP. Calculate the…

Q: Two bars in the form of a single crystal of pure tin present elastic limits significantly different…

A: elastic limit significantly different at 0.2% of compensated strain value then

Q: The yield strength for an alloy that has an average grain diameter of 4.7 x 10² mm is 134 MPa. At a…

Q: What are slipbands and slip lines? What causes the formation of slipbands on a metal surface? What…

Q: Calculate the typical relaxation time for silicate glassand comment on its propensity for stress…

A: Given: E=70 GPaη=1×1012GPa-s

Q: How do you increase the hardness of components being made from 0.8% carbon steel? Explain the…

A: Solution:

Q: • A 850-lb force is applied to a o.15-in. diameter nickel wire having a yield strength of 45,000 psi…

A: Find the stress and determine the wire will deform plastically or not.

Q: How do you increase the hardness of components being made from 0.8% carbon steel? Explain the…

A: Solution:

Question

The yield point for a brass alloy that has an average grain diameter of 50 micrometers is 120 MPa.

The yield point for a brass alloy that has an average grain diameter of 50 µm is 120 MPa. At a grain diameter of 10 µm, the yield point increases to 240 MPa. At what
grain diameter (in µm) will the yield point be 200 MPa?

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

The yield strength for an alloy that has an average grain diameter of 5.2 x 102 mm is 110 MPa. At a grain diameter of 6.3 x 103 mm, the yield strength increases to 251 MPa. At what grain diameter, in mm, will the yield strength be 222 MPa? d = mm
Question The yield strength for an aluminum alloy that has an average grain diameter of 10 um is 400 MPa. As the grain diameter is increased to 80 um, the yield strength decreases to 260 MPa. When the grain diameter is 2 um, its yield strength is close to 760 MPa 668 MPa 566 MPa 419 MPa
Consider a single crystal of BCC iron oriented such that tensile stress is applied along a[010] direction. Compute the resolved shear stress along a (110) plane and in a [1⃑ 1 1]direction when a tensile stress of 50 MPa is applied. If Slip occurs on a (110) plane and ina [1⃑ 1 1] direction and the critical resolved shear stress is 25 MPa, calculate themagnitude of the applied tensile stress necessary to initiate yielding.
3. Molybdenum has a BCC crystal structure, an atomic radius of 0.1363 nm, and an atomic weight of 95.94 g/mol. Compute its theoretical density.4. For a brass alloy, the stress at which plastic deformation begins is 345 MPa and the modulus of elasticity is 103 GPa.a. What is the maximum load that may be applied to a specimen with a cross-sectionalarea of 130 mm2 without plastic deformation?b. If the original specimen length is 76 mm, what is the maximum length to which itmay be stretched without causing plastic deformation?
The average grain diameter and yield strength for a brass material were measured as a function of time at 650°C. Given the following yield strengths for the two specimens, compute the heat treatment time required at 650°C to give a yield strength of 100 MPa. Assume a value of 2 for n, the grain diameter exponent. Time (min) 30 90 Yield Strength (MPa) 90 75 min Grain Diameter (mm) 3.9 x 10-2 6.6 x 10-2
Help me please
A 1.02den silk fiber has reached its maximum tenacity value. How many grams (force) would it take to rupture such fiber when dry? Provide your answer with two (2) decimal positions and no unit Answer:
1. Consider a single crystal of BCC iron oriented such that a tensile stress is applied along a [010] direction. Compute the resolved shear stress along a (110) plane and in a direction when a tensile stress of 52 MPa (7500 psi) is applied. Slip plane (110) Normal to Slip direction [111] slip plane y Direction of applied stress [010] 2. Compute the tensile strength and ductility (%EL) of a cylindrical copper rod if it is cold worked such that the diameter is reduced from 15.2 mm to 12.2 mm (0.60 in. to 0.48 in.). 3. Please explain the differences between recovery and recrystallization processes.
3) The strength of a titanium piece is found to be 65,000 psi when the grain size is 17 x10-6 m and 82,000 psi when the grain size is 0.8 x10 m. What would be the 9- (a) Constants in the Hall-Petch equation Strength of this titanium piece when the grain size is reduced to 0.2 x10 m. (9)
The yield strength for an alloy that has an average grain diameter of 5.3 x 10 146 MPa. At a grain diameter of 7.8 × 10-3 mm, the yield strength increases to 249 MPa. At what grain diameter, in mm, will the yield strength be 236 MPa? d = Ex 0.0022 mm Check Try again 1
A single crystal of a metal that has the FCC crystal structure is oriented such that a tensile stress is applied parallel to the [100] direction. If the critical resolved shear stress for this material is 1.18 MPa, calculate the magnitude of applied stress necessary to cause slip to occur on the (111) plane in the [1-10] direction.
The yield stresses (σY) have been measured using steel and aluminum specimens of various grain sizes given in the attached image.On the basis of data answer the following questions: (a) Determine the coefficients σ0 and kY in the Hall- Petch for these two materials.(b) Determine the yield stress in each material for a grain size of d=26 μm.