Interpretation: The mechanism by which chemistry and engineering helped transform aluminum from a precious metal into an inexpensive structural material should be explained.
Concept Introduction:
Aluminum is known to be the world’s most abundant metal. It is the third most common element and present as the 8% of the earth’s crust. It is derived from the mineral bauxite.
Pure form of aluminum is soft, corrosion resistant, ductile and has a high electrical conductivity. It is used as foil and conductor cables by alloying with other metals in order to give strength to it. It is known to be the lightest engineering metal with strength to weight ratio. More than the steel, this makes aluminum an important structural material. Opposite to steel, the strength of aluminum increases on decreasing temperature. Thus, aluminum works well in the cold atmosphere. For pure aluminum, the tensile strength is 90 MPa which is increased to 680 MPa for the aluminum alloys treated with heat.
Explanation of Solution
The increase in application of the aluminum is due to its properties such as strength, recyclability, lightness, formability and resistance to corrosion. The types of product ranges from the packaging foils to the structural materials.
Aluminum is generally alloyed with metals such as magnesium, zinc, copper, manganese, silicon, and lithium. Other metals such as titanium, chromium, lead, nickel and bismuth are also added in small quantities.
The tensile strength of pure aluminum is low, after the addition of other metals for alloying, the strength of the aluminum increases.
Mechanisms for strengthening aluminum:
The engineering applications commonly for aluminum includes automotive, aerospace, buildings, beer and soda cans. Since, the pure aluminum is soft, the strengthening of aluminum is important to use it for engineering structures.
The strength of aluminum is modified with the help of the cold working, heat treating and alloying. Generally, the strength of alloys can be increased by cold working but some of the alloys required additional strength and undergoes solid solution strengthening, precipitation strengthening, and dispersion strengthening.
Cold working: This reduces the material thickness. The sheets and plates of different thickness are made with the help of cold rolling. Generally, the strength of all the aluminum alloy can be increased by cold working.
Solid solution strengthening: The strength of metal increases when any alloying element is added to the aluminum. The mixture so formed is called a solid solution as the aluminum is mixed with the alloying atoms. The strengthening extent depends on the type and percentage of alloying elements added to the aluminum.
Precipitation strengthening: The particles with size less than 0.001 mm are formed inside the metal in this process. The particles are known as precipitates and contain the aluminum compounds with alloying elements or alloying elements compounds. This is due to the series of heat treatment. When the precipitate is formed, the step is known as aging.
Dispersion strengthening: In the aluminum casting process, when alloy of manganese reacts with aluminum and silicon and iron, the dispersoid particles are formed. The diameter of these particles is less than 0.001 mm. The grain structure is influenced by the dispersoid particles which is formed during the heat treatment. This results in the increase strength of alloy as compared to the one formed without dispersoids.
Want to see more full solutions like this?
Chapter 1 Solutions
Chemistry for Engineering Students
- 4.48 Elemental phosphorous is used in the semiconductor industry. It can be obtained from an ore called fluoroapatite via reaction with SiO2 and C: 4Ca5( PO4)3F+18SiO2+30C3P4+30CO+18CaSiO3+2CaF2 Suppose a particular semiconductor production plant requires 1500 kg of P4. If the recovery of P4 from this reaction is 73% efficient, what mass of fluoroapatite is needed?arrow_forwardPhosphorus occurs naturally in the form of fluorapatite, CaF2 3Ca3(PO4)2. The dot indicates 1 part CaF2 to 3 parts Ca3(PO4)2. This mineral is reacted with an aqueous solution of H2SO4 in the preparation of a fertilizer. The products are phosphoric acid, hydrogen fluoride, and gypsum, CaSO4 2H2O. Write the balanced equation describing this process.arrow_forwardThree reactions very important to the semiconductor industry are The reduction of silicon dioxide to crude silicon, SiO2(s) + 2 C(s) → Si(s) + 2 CO(g) ΔrH° = 689.9 kJ/mol The formation of silicon tetrachloride from crude silicon, Si(s) + 2 Cl2(g) → SiCl4(g) ΔrH° = −657.01 kJ/mol The reduction of silicon tetrachloride to pure silicon with magnesium, SiCl4(g) + 2 Mg(s) → 2 MgCl2(s) + Si(s) ΔrH° = −625.6 kJ/mol Calculate the overall enthalpy change when 1.00 mol sand, SiO2, changes into very pure silicon by this series of reactions.arrow_forward
- Complete and balance the equations of the following reactions, each of which could be used to remove hydrogen sulfide from natural gas: (a) Ca(OH)2(s)+H2S(g) (b) Na2CO3(aq)+H2S(g)arrow_forwardAluminum is produced commercially by the electrolysis of Al2O3 in the presence of a molten salt. If a plant has a continuous capacity of 1.00 million A, what mass of aluminum can be produced in 2.00 h?arrow_forwardHow many kilojoules of heat will be released when exactly 1 mole of manganese, Mn, is burned to form Mn3O4(s) at standard state conditions?arrow_forward
- The amount of sodium hypochlorite in a bleach solution can be determined by using a given volume of bleach to oxidize excess iodide ion to iodine; ClO- is reduced to Cl-. The amount of iodine produced by the redox reaction is determined by titration with sodium thiosulfate, Na2S2O3; I2 is reduced to I-. The sodium thiosulfate is oxidized to sodium tetrathionate, Na2S4O6. In this analysis, potassium iodide was added in excess to 5.00 mL of bleach (d=1.00g/cm3) . If 25.00 mL of 0.0700 M Na2S2O3 was required to reduce all the iodine produced by the bleach back to iodide, what is the mass percent of NaClO in the bleach?arrow_forwardThe following reactions are all similar to those of the industrial chemicals. Complete and balance the equations for these reactions: (a) reaction of a weak base and a strong acid. NH3+HClO4 (b) preparation of a soluble silver salt for silver plating. Ag2CO3+HNO3 (c) preparation of strontium hydroxide by electrolysis of a solution of strontium chloride SrCl2(aq)+H2O(l)electrolysisarrow_forward
- Chemistry for Engineering StudentsChemistryISBN:9781285199023Author:Lawrence S. Brown, Tom HolmePublisher:Cengage LearningChemistry: The Molecular ScienceChemistryISBN:9781285199047Author:John W. Moore, Conrad L. StanitskiPublisher:Cengage LearningIntroductory Chemistry: An Active Learning Approa...ChemistryISBN:9781305079250Author:Mark S. Cracolice, Ed PetersPublisher:Cengage Learning
- Chemistry: Matter and ChangeChemistryISBN:9780078746376Author:Dinah Zike, Laurel Dingrando, Nicholas Hainen, Cheryl WistromPublisher:Glencoe/McGraw-Hill School Pub CoGeneral Chemistry - Standalone book (MindTap Cour...ChemistryISBN:9781305580343Author:Steven D. Gammon, Ebbing, Darrell Ebbing, Steven D., Darrell; Gammon, Darrell Ebbing; Steven D. Gammon, Darrell D.; Gammon, Ebbing; Steven D. Gammon; DarrellPublisher:Cengage LearningChemistry for Engineering StudentsChemistryISBN:9781337398909Author:Lawrence S. Brown, Tom HolmePublisher:Cengage Learning