(a)
The ultimate tensile stress of metal specimen.
Answer to Problem 1.5.1P
Explanation of Solution
Given:
The diameter of metal specimen is
The load at facture is
Concept Used:
Write the equation to calculate the ultimate tensile stress.
Here, ultimate tensile stress is
Calculation:
Calculate the cross-sectional area of specimen.
Here, diameter of the specimen is
Substitute
Calculate the ultimate tensile stress.
Substitute
Conclusion:
Thus, the ultimate tensile stress on the metal specimen is
(b)
The elongation of the metal specimen.
Answer to Problem 1.5.1P
Explanation of Solution
Given:
The original gage length is
The change in gage length is
Concept Used:
Write the equation to calculate the elongation.
Here, the elongation is
Calculation:
Calculate the elongation of the metal specimen.
Substitute
Conclusion:
Thus, the elongation of the metal specimen is
(c)
The reduction in the cross-sectional area of the metal specimen.
Answer to Problem 1.5.1P
Explanation of Solution
Given:
The original diameter of metal specimen is
The diameter after fracture load is
Concept Used:
Write the equation to calculate reduction in cross-sectional area.
Here, the reduction in cross-sectional area is
Calculation:
Calculate the cross-sectional area after fracture load.
Substitute
Calculate the reduction in the cross-sectional area.
Substitute
Conclusion:
Thus, the reduction in the cross-sectional area is
Want to see more full solutions like this?
Chapter 1 Solutions
Steel Design (Activate Learning with these NEW titles from Engineering!)
- A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.arrow_forwardA tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.arrow_forward5. A tensile test was done on a magnesium sample of original diameter and original length of 12mm 30mm respectively. The final length and diameter were 32.61mm and 11.74mm respectively. Plot the stress versus strain graph and determine: a. 0.2% proof stress b. Tensile strength c. % elongation d. % reduction e. Stress at fracture f. Modulus of Elasticity. 66 Force (N) Ext. 0.0112 0.0157 0.0199 0.0240 1.72 (mm) 177 327 462 797 1350 1720 2220 2690 2690 5.55 8.15 13.07 22.77 25.25arrow_forward
- The following observations were made during a tensile test on a mild steel specimen 40 mm in diameter and 200 mm long. Elongation is with 40 kN load (with in limit of proportionality) 8=0.0304mm, yield load = 161 kN, Maximum load = 242 kN Length of specimen at fracture = 249mm Find: 1) Young's Modulus of elasticity ; E 2) Yield point stress Ultimate stress 3) 4) Percentage elongationarrow_forwardA1 Copy the sketch of the tensile stress-strain test (Figure A1) results for a waisted metallic specimen and indicate the locations representing maximum stress (A), ultimate strain to failure (B), and 0.2% proof (yield) stress (C), and calculate the Young's modulus of the material. Figure A1 300 250 200 150 100 50 0 Stress (MPa) 0.2 0.4 0.6 8.0 Strain (%) 10.0arrow_forwardThe brinell hardness test was performed on a steel sample using a 5mm indenter diameter, and the indentation diameter was 2 mm, calculate brinell hardness number?arrow_forward
- 1 a. During a tensile test on a specimen the following results were obtained: Load (kN) 15 |30 40 50 55 60 Extension 1.03 2.00 2.73 3.42 3.80 4.10 (mm) Diameter of gauge length =19mm Gauge length = 150mm Load at fracture = 80kN Diameter at fracture =16.5mm Gauge length at fracture = 170mm Ultimate load = 120kN Plot the load/extension graph to an appropriate scale. Hence determine the Modulus of elasticity ii. Percentage elongation iii. Percentage reduction in area iv. The nominal stress at fracture v. The actual stress at fracture vi. Ultimate tensile strength i.arrow_forwardQuestion 4. A tensile test is carried out on a bar of mild steel of diameter 2 cm. The bar yields under a load of 80 Kn. It reaches a maximum load of 150 kN, and breaks finally at a load of 70 kN. Estimate: a)the tensile stress at the yield point b)the ultimate tensile stress c)the average stress at the breaking point if the diameter of the fractured neck is 1 cm.arrow_forwardA cylindrical metal specimen having an original diameter of 11.26 mm and gauge length of 53.3 mm is pulled in tension until fracture occurs. The diameter at the point of fracture is 6.99 mm, and the fractured gauge length is 66.2 mm. Calculate the ductility in terms of (a) percent reduction in area (percent RA), and (b) percent elongation (percent EL).arrow_forward
- A metal specimen with a square cross-sectional area having a gauge length of 50.0 mm is pulled in tension.If its width at the point of fracture is 5 mm and fractured gauge length is 75 mm. Calculate the ductility interms of:a) percent elongation b) percent reduction in area (Assume that its original width is 9 mm.)arrow_forwardDuring a tensile test on a specimen of steel the following data was recorded, diameter of specimen 6.6mm gauge length of 50mm ,elongation of a load of 6.0 KN of 0.043mm. Reduction of area at failure of 45percent. Calculate the youngs modulus of elasticity ,the yield stress and the ultimate stressarrow_forwardThe following observations were made during a tensile test on a mild steel specimen 40 mm in diameter and 200 mm long. Elongation with 40 KN load (within limit of proportionality) Change in length=0.0202 mm. Determine stress and strain valuearrow_forward
- Steel Design (Activate Learning with these NEW ti...Civil EngineeringISBN:9781337094740Author:Segui, William T.Publisher:Cengage LearningMaterials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning