(a)
The work done in expanding a
(a)
Answer to Problem 2.81P
The work done in expanding a
Explanation of Solution
Given:
Thickness of shell is
Initial diameter is
Final diameter is
The stress for material is
Concept used:
Write the expression for true strain for shell.
Here,
Write the expression for specific energy for balanced biaxial plane stress condition.
Substitute
Here,
Write the expression for work done.
Here,
Substitute
Simplify above expression.
Write the expression for stress for material.
The true strain is obtained by integrating the above expression.
After integration simplify above expression.
Calculation:
Substitute
Substitute
Substitute
Conclusion:
Thus, the work done in expanding a
(b)
Explain the dependency of answer on yield criterion.
(b)
Explanation of Solution
In this case, the amount of tension applied on biaxial stress plane is equal in magnitude and in biaxial plane with equal stresses the yield criterion for both maximum shear stress theory and distortion energy gives same result.
Thus, the answer is not dependent on any yield criterion.
Want to see more full solutions like this?
Chapter 2 Solutions
EBK MANUFACTURING PROCESSES FOR ENGINEE
- For a tensile test it can be shown that the percent cold work (%CW) is related to strain according to the following relationship: %CW=(εε+1) × 100 Using this equation, compute the percent cold work experienced by naval brass (for which the stress-strain behavior is shown in the Animated Figure 6.12) when a stress of 415 MPa (60190 psi) is applied.arrow_forwardA steel plate, which has a fracture toughness in a plane strain state of 83 MPavm, is alternately loaded in tension at 750 MPa and in compression at 20 MPa. The plate must survive 15 years with the stress applied at a frequency of once every 3 min. Calculate the constant C of the material if n=2.8 . Assume that the geometric factor f=1 for all your imperfections. Internal imperfections have a size of 0.0015 mmarrow_forwardThe ultimate tensile strength of a material is 400 MPa and the elongation up to maximum load is 35%. If the material obeys power law of hardening, then the true stress-true strain relation (stress in MPa) in the plastic deformation range is (b) o = 775 ɛ0.30 (d) o = 775 ɛ0.35 (a) o = 540ɛ0.30 %3D (c) o = 540 ɛ0.35 %3D %3Darrow_forward
- A 30-mm-diameter popper rod is 1 m long with a yield strength of 70 MPa. Determine the axial force necessary to cause the diameter of the rod to reduce by 0.01 percent, assuming elastic deformation. Check that the elastic deformation assumption is valid by comparing the axial stress to the yield strength.arrow_forwardThe compressive strength of alumina quartz (Al2O3) is 2.1 GPa. A quartz tube is being used for a vacuum furnace. Both ends of the tube are constrained and cannot move. To what temperature can the tube be heated up from room temperature such that the tube won’t fracture due to the thermal stress?arrow_forwardA copper wire is stretched elastically with a stress of 70 MPa at 20°C. If the length is held constant, to what temperature must the wire be changed to reduce the stress to 35 MPa?arrow_forward
- A copper sample exhibits work-hardening described by where σ0 = 50 MPa, n = 0.5, K = 500 MPa. Calculate the temperature rise when the sample is deformed up to a strain of 0.2. Assume that the conversion factor is 1.0, and given: density = 8.9 g/cm3; heat capacity = 360 J/kg Karrow_forwardWhat results do we get when shear stress is applied to homogeneous isotropic material?arrow_forwardThe yield stresses (σY) have been measured using steel and aluminum specimens of various grain sizes given in the attached image.On the basis of data answer the following questions: (a) Determine the coefficients σ0 and kY in the Hall- Petch for these two materials.(b) Determine the yield stress in each material for a grain size of d=26 μm.arrow_forward
- QUESTION 2 (a) Stress and strain diagram of 316L stainless steel is plotted in Figure Q2 (a). Determine and label the following terms: (i) Proportional limit point (0,ɛ) (ii) Yield point (0,ɛ) (iii) Ultimate point (0,8) (iv) Fracture point (0,8) (iv) Modulus of elasticity or Young's modulus (E) 700 400 600 500 300 400 200 6 300 200 E 100 100 0.005 0.01 0.015 0.02 0.05 0.1 0.15 0.2 0.25 0.3 0.35 0.4 0.45 Strain, E (mm/mm) Strain, E (mm/mm) Figure Q2 (a) (b) A short post AB constructed from a hollow circular tube of aluminium, supports a compressive load of 116 kN as in Figure Q2 (b). The inner and outer diameters of the tube are di=100 mm and dz=112 mm, respectively, and its length is 400 mm. The shortening of the post due to the load is measured as 0.3 mm. Determine the compressive stress and strain in the post. Note: the weight of the post is neglected. 116 KN A 400 mm Figure Q2 (b) Stress, o (MPa) Stress, a (MPa)arrow_forwardFind the total toughness energy for a metal that experiences both elastic and plastic deformations. The modulus of elasticity is 107.2 GPa, and elastic deformation terminates at a strain of 0.009. For plastic deformation, assume that the relationship between stress and strain is described by T = 1.66xKn, in which the values for K and n are 1453 MPa and 0.175, respectively. Furthermore, plastic deformation occurs between strain values of 0.009 and 0.67, at which point fracture occursarrow_forwardConsider a metal rod with a critical resolved shear stress of 40 MPa for a specific crystallographic plane (hkl). The angle between the normal to the plane and the applied force is 30 degrees, and the angle between the slip direction and the force is 15 degrees. Two force levels of F1 = 75 N and F2 = 40 N is applied. The cross-sectional area of the rod is 1 mm^(2). Will the slip initiate at the two force levels? Select one: O a. F1: Yes, F2: No O b. F1: Yes, F2: Yes O C. F1: No, F2: Yes d. F1: No, F2: Noarrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY